Ровинг прямой для технологий намотка и пултрузия JUSHI EDR24-2400-386

386 Direct Roving is coated with a silane-based sizing compatible with unsaturated polyester, vinyl ester, and epoxy resins. It is designed for filament winding, pultrusion, and weaving applications.

386 is suitable for use in pipes, pressure vessels, gratings, and profiles and the woven roving converted from it is used in boats and chemical storage tanks.

Product Features

  • Good process performance and low fuzz
  • Compatibility with multiple resin systems
  • Complete and fast wet-out © Good mechanical properties


Glass Type
Type of Size
Type of Size
Linear Density (tex)
Filament Diameter (ui)


300-735 200-400 600 900 1100-1200 1500 1700 2200 2400-4800 9600
114 16 17 17 17 18 19 22 24 31


Technical Parameters

Linear Density (%)

ISO 1889

Moisture Content (%) Size Content (%) Breakage Strength (N/tex)

ISO 3344 ISO 1887 ISO 3341
<0.10 0.55±0.15 >0.40


Mechanical Properties

Mechanical Properties

Tensile Strength
Tensile Modulus

Unit Value Resin Method

MPa 1970 Polyester ASTM D2343
MPa 78794 Polyester ASTM D2343


The above data are actual experimental values for EDR24-2400-386 and for reference only.

Unless otherwise specified, the fiberglass products should be stored in a dry, cool and moisture-proof area. The room temperature and humidity should be always maintained at 15eC~35eC and 35% ~ 65%. It is best if the product is used within 12 months after production date.The fiberglass products should remain in their original packaging until just prior to user .