Ровинг прямой для технологий намотка и пултрузия JUSHI EDR24-2400-386

386 Direct Roving is coated with a silane-based sizing compatible with unsaturated polyester, vinyl ester, and epoxy resins. It is designed for filament winding, pultrusion, and weaving applications.

386 is suitable for use in pipes, pressure vessels, gratings, and profiles and the woven roving converted from it is used in boats and chemical storage tanks.

Product Features

  • Good process performance and low fuzz
  • Compatibility with multiple resin systems
  • Complete and fast wet-out © Good mechanical properties

Identification

Glass Type

E

Type of Size

Silane

Size Code

386

Linear Density (tex)

300

735

200

400

600

900

1100

1200

1500

1700

2200

2400

4800

9600

Filament Diamete (ui

114

16

17

17

17

18

19

22

24

31

Technical Parameters

Linear Density (%)

Moisture Content (%)

Size Content (%)

Breakage Strength (N/tex)

ISO 1889

ISO 3344

ISO 1887

ISO 3341

±5

<0.10

0.55±0.15

>0.40

Mechanical Properties

Mechanical Properties

Unit

Value

Resin

Method

Tensile Strength

MPa

1970

Polyester

ASTM D2343

Tensile Modulus

MPa

78794

Polyester

ASTM D2343

The above data are actual experimental values for EDR24-2400-386and for reference only.

Packegin

Storage

Pallet length mm (in)

1120 (44)

1270 (50)

Pallet width mm (in)

1120 (44)

960 (37.8)

Pallet height mm (in)

940 (37)             1180 (46.5)

940 (37)               1180 (46.5)

* The product can be packed on pallet or in small cardboard boxes.

Package height mm (in)

260 (10)

260 (10)

Package inside diameter mm (in)

160 (6.3)

160 (6.3)

Package outside diameter mm (in)

270 (10.6)

310 (12.2)

Package weight kg (lb)

15.6 (34.4)

22 (48.5)

Number of layers

3

4

3

4

Number of doffs per layer

16

12

Number of doffs per pallet

48

64

36

48

Net weight per pallet kg (in)

750 (1653.4)

1000 (2204.6)

792 (1746)

1056 (2328)

Unless otherwise specified, the fiberglass products should be stored in a dry, cool and moisture-proof area. The room temperature and humidity should be always maintained at 15eC~35eC and 35% ~ 65%. It is best if the product is used within 12 months after production date.The fiberglass products should remain in their original packaging until just prior to user .

To ensure safety and avoid damage to the product, the pallets should not be stacked more than three layers high. When the pallets are stacked in 2 or 3 layers, special care should be taken to correctly and smoothly move the top pallet.